Unialloy HF 960

Weld Deposits with Exceptionally High Wear Resistance to Abrasion at Elevated Temperatures

Basic Details

Name

Unialloy HF 960

Category

Hard Facing

Key Features

Microstructure - Premium Carbides in Tough Austentic Matrix
Excellent Wear Resistance to Abrasion, Corrosion and Erosion at High Temperatures up to 600^oC
Very High Deposit Efficiency

Welding Position

All Positions

Industries

Cement, Iron & Steel, Sugar, Thermal Power

Hardness

61 - 65 RC, 66 - 70 RC

Download brochure

Advance Details

Technical Characteristics:
Hardness – 63-68 RC

Typical Application:
Sinter Breaker, Burner Nozzles/Ducts, Mill Discharge Valves, Rail Tie, Tamper Tips, ID Fan Blades, Hot Slag Conveyors, Slurry Pump.

Application Procedure:
Remove all surface contamination and fatigue material from weld area. Use stringer bead or weaving technique for deposit of weld material. Remove slag between multiple passes. Do not allow excessive heat built up. For austenitic manganese steel inter-pass temperature should not exceed 150^oC. Allow to cool down slowly.

Current: AC/DC +

Size(mm): 4.00, 3.15

Welding Parameters

Size (mm)	4.0	3.15
Amps	140-210	125-165